17-7PH ukuqina (RH950) izinga lokushisa eliphansi lokucisha + ukuguga
17-7PH noma Uhlobo 631 (UNS S17700) luyinsimbi eqinile ye-chromium-nickel aluminium esetshenziswa ekusetshenzisweni kwentwasahlobo ezimbonini eziningi.
Ama-alloys aqinisa imvula angu-7-7 angakhiwa esimweni esithambile se-austenitic futhi abe lukhuni kumazinga wamandla aphezulu ngokwelashwa kokushisa okuphansi. Izinga lokushisa eliphansi livumela ukuguqulwa okuncane uma kuqhathaniswa nokucisha okuvamile kanye nezinqubo zokuqina kwentukuthelo. Esimweni esithambile se-austenitic annealed, 17-7 yakhekeka kakhulu futhi ilungele imisebenzi efana nokudweba, ukugoba, kanye nokwakheka ekugcineni. I-17-7 ikwazi ukushisela kalula kuzo zombili izimo ezifakwe emanzini kanye nezingelashwa ngokushisa.
I-Element:
Ikhabhoni: 0.09 max
I-Manganese: 1.00 max
I-Phosphorus: 0.040 max
Isibabule: 0.030 ubuningi
I-silicon: 1.00 max
I-Chrome: 16.00 - 18.00
I-Nickel: 6.50 - 7.75
I-Aluminium: 0.75 - 1.50
Insimbi: Ibhalansile
Izinto ezibonakalayo:
Iphuzu elincibilikayo: 2550 – 2640°F (1400 – 1450°C)
Ukuminyana: 0.282 lb/in3 / 7.8 g/cm3
I-Tensile Modulus ye-Elasticity (RH 950 ne-TH 1050): 29.6 X 10 6 psi / 204 GPA
Ukuziphatha kwemishini:
Isimo: annealed
I-Tensile Strength Minimum (psi): 130,000
Isivuno Amandla Min. 0.2% Offset (psi): 40,000
2″ Ubude obujwayelekile: 35%
Ukuqina: Rockwell B85
Isimo: lukhuni + ubudala (TH1050)
Amandla Okuqina Okuqinile (psi): 200,000
Amandla Esivuno Okujwayelekile okungu-2% Shift (psi): 185,000
% ubude ku-2″: 9%
Ukuqina: Rockwell C40
Isimo: lukhuni, izinga lokushisa eliphansi lokucisha + ukuguga (RH950)
Amandla Okuqina Okuqinile (psi): 235,000
Amandla Esivuno Okuvamile okungu-2% uhambo (psi): 220,000
% ubude ku-2″: 6%
Ukuqina: Rockwell C48
Isimo: Okubandayo Okugoqiwe/Kusebenzile + Ubudala (CH900)
Amandla Okuqina Okuqinile (psi): 265,000
Amandla Esivuno Okuvamile okungu-2% uhambo (psi): 260,000
% ubude ku-2″: 2%
Ukuqina: Rockwell C49
ukwelashwa ukushisa:
17-7 idinga izinyathelo ezintathu eziyisisekelo ekwelapheni ukushisa:
I-Austenitic conditioning.
Ukupholisa kuguqula i-austenite ibe yi-martensite
Imvula iba nzima ibe yizimo ezingu-TH 1050 noma i-RH 950
Kungenjalo, ukuze kutholwe izakhiwo eziphakeme kakhulu zemishini ku-alloy, isimo A siguqulwa sibe yi-martensite ngokunciphisa amakhaza sibe ku-C kumshini wokugaya. Ukwenza lukhuni esimweni esingu-CH 900 kufezwa ukwelashwa okukodwa okunezinga lokushisa eliphansi lokuguga.