I-UNS C68700 Aluminium Brass
I-UNS C68700/CDA 687/CW702R/CZ110/CuZn20A12As Ilungele ukumelana nokugqwala okuhle kakhulu kanye nokusebenza okubandayo okuhle kakhulu kokwakheka nokugoba.
Elements | ||||||
---|---|---|---|---|---|---|
Cu(1,2) | Pb | Zn | Fe | Al | As | |
(1) Inani le-Cu lihlanganisa u-Ag. (2) Cu + Isamba Sezinto Eziqanjiwe 99.5% min. |
||||||
Ubuncane (%) | 76.0 | 1.8 | 0.02 | |||
Ubukhulu (%) | 79.0 | 0.07 | o gavriliuk ir kvitka | 0.06 | 2.5 | 0.06 |
Izakhiwo zemishini:
Ifomu | I-Temper | Ikhodi Yesimo | Amandla Amandla (ksi) |
YS-0.5% Ext (ksi) |
Ukuphakanyiswa (%) |
Isilinganiso se-Rockwell F |
---|---|---|---|---|---|---|
* Kukalwa ekamelweni lokushisa, 68°F (20°C). | ||||||
I-Tube | Usayizi Wokusanhlamvu Okujwayelekile 0.025 mm | OS025 | 60 Uhlobo | 27 Uhlobo | 55 Uhlobo | 77 Uhlobo |
Izakhiwo Zomzimba:I-Melting Point - i-Liquidus° F: 1780
I-Melting Point - i-Solidus° F: 1710
Ukuminyana lb/cu in. ku-68°F: 0.301
Ubukhulu obukhulu: 8.33
Ukusebenza kukagesi% IACS ku-68°F: 23
Ukuqhuba UkushisaI-Btu/ sq ft/ ft hr/ °F ku-68°F: 58
I-Coefficient of Thermal Expansion 68-572Amandla ayi-10 kuye ku-6 °F ngayinye (68 - 572°F): 10.3
Amandla Okushisa athizeI-Btu/ lb /°F ku-68°F: 0.09
I-Modulus of Elasticity in Tension ksi: 16000
I-Modulus ye-Rigidity ksi: 6000
Izinto ezilinganayo ne-UNS C68700 arsenical aluminium brass alloy yilezi:
I-ASME SB111
I-ASME SB359
I-ASME SB395
I-ASME SB543
I-ASTM B111
I-ASTM B359
I-ASTM B395
I-ASTM B543
Amandla
Isilinganiso sokusebenza kwe-UNS C68700 singama-30.
Welding
I-soldering, i-brazing, i-oxyacetylene welding, i-gas shieded arc welding, i-spot welding, i-seam welding, kanye ne-butt welding kuthathwa njengezinqubo ezifanele zokushisela, kanti izinqubo ezifana nokushisela i-arc yensimbi ehlanganisiwe azinconywa kuma-alloys e-UNS C68700.
Kuyashisa Ukusebenza
Amandla okusebenza ashisayo e-UNS C68700 afanelekile ngezinga lokushisa elifanele elishisayo eliphakathi kuka-760 no-871.1°C (1400 no-1600°F).
Ukusebenza Okubandayo
I-UNS C68700 inomthamo omuhle kakhulu wokusebenza obandayo.
Annealing
Izinga lokushisa le-anneal ye-UNS C68700 liphakathi kuka-427 no-593°C (800 no-1100°F).