I-UNS N08028/EN 1.4563/Ingxubevange 28 yensimbi engagqwali
Ingxubevange 28 amapuleti ensimbi, ingxubevange 28 imigoqo yensimbi engagqwali
Ngokufana ne-Sandvik Sanicro 28, i-alloy 28 iwuhlobo lwe-ultra-low carbon nickel-iron-chromium Austenite alloy enezengezo ze-molybdenum nethusi futhi iyizinga lensimbi engagqwali elinokuqukethwe okuphezulu kwe-nickel. Inokumelana nokugqwala okuhle endaweni ene-asidi eqinile kanye nokumelana nokuqhekeka kokugqwala kwengcindezi endaweni ye-hydrogen sulfide (H2S) kanye ne-chloride. Ngaphezu kwalokho, futhi inokumelana okuhle kakhulu nokugoba, ukuqhekeka, i-intergranular, ukugqwala kwengcindezi nokuqhekeka, kanye nokushisela okuhle. Ngenxa yalezi zakhiwo zokugqwala ezivelele, i-alloy 28 ingasetshenziswa ezindaweni ezihluke kakhulu.
Ingxubevange 28 amabanga alinganayo:
I-American: I-Incoloy 028, i-alloy 28, i-UNS N08028,
Chinese: 00Cr27Ni31Mo3Cu, 00Cr27Ni31Mo4Cu
German:1.4563 – X1NiCrMoCu31-27-4
Amafomu Atholakalayo kanye Nemininingwane:
Ishubhu nepayipi: ASTM B 668, EN 10216-5, SEW 400 (Feb 1991), SS 14 25 84, NFA 49-217
Ipuleti, ishidi, kanye nomdweshu: ASTM B 709, EN 10088
Ibha: EN 10088-3, EN 10272, SS 14 25 84
Ukufakwa: ASTM A403
Ukwakhiwa kwama-Chemical:
Material | C | Si | Mn | Cr | Ni | Mo | P | S |
N08028 | ≤0.03 | ≤1.0 | ≤2.5 | 26.0 ~ 28.0 | 29.5 ~ 32.5 | 3.0 ~ 4.0 | ≤0.03 | ≤0.03 |
1.4563 | ≤0.02 | ≤0.7 | ≤2.0 | 26.0 ~ 28.0 | 30.0 ~ 32.0 | 3.0 ~ 4.0 | ≤0.03 | ≤0.01 |
Izici zemishini:
Ukuminyana, g/cm³ | 8.0 |
Ibanga lokuncibilika, °C | 1350 - 1370 |
Amandla aqinile, min, Mpa | 650 |
Amandla esivuno, 0.2% offset, min, Mpa | 250 |
Ukwelulwa, %, imiz | 40 |
Ubulukhuni, HB | 155 |
Izicelo:
I-alloy28 ekuqaleni yasungulwa ukuze ixazulule i-wet-process phosphoric acid heat exchanger material. Ukumelana nokugqwala kwayo okuhle kakhulu kuyenza ikwazi ukumelana nokugqwala kwe-H2S, i-chloride, i-phosphoric acid, kanye ne-sulfuric acid corrosion resistance, esetshenziswa kabanzi kokuqukethwe okuphezulu kwe-H2S ekuxhashazweni kwensimu kawoyela negesi, uhlelo lwe-flue gas desulfurization, Amanzi olwandle namanzi okupholisa ane-chloride, imboni yokwenza amaphepha, i-phosphoric acid kanye ne-organic acid kanye nedivayisi yokukhiqiza i-ester synthesis, iyinto ekahle esetshenziselwa ukufaka esikhundleni sokushintshanisa ukushisa kwegraphite ku-phosphoric acid egxilile.
I-LKALLOY ingumnikezeli ohamba phambili embonini wochungechunge lwe-Cr-Ni namanye ama-alloys ensimbi engagqwali ekhwalithi ephezulu. I-LKALLOY ihlinzeka nge-alloy 28 ipayipi neshubhu, induku eyayisetshenziselwa izinhlelo zokusebenza eziningana njengama-condensers, izishintshi zokushisa, izihlungi, nokuningi.