I-Titanium Grade2, CP Gr.2
I-Titanium Grade2(UNS R50400) iyibanga elisetshenziswa kakhulu le-CP (Commercially Pure) Titanium. I-CP titanium equkethe ngaphezu kuka-99% Ti. Ukuminyana kwe-Titanium Gr2 cishe kucishe kube ngu-50% kokwama-nickel alloys nezinsimbi ezingenasici. Isetshenziswa kabanzi ekusetshenzisweni kolwandle, uwoyela negesi kanye namakhemikhali. I-LKALLOY ihlinzeka ngokuyinhloko ngamashubhu e-Titanium Grade 2, ishidi le-Titanium Grade2 kanye nebha eyindilinga ye-Titanium yeBanga lesi-2 ngosayizi nokucaciswa okuhlukahlukene.
Amafomu Atholakalayo kanye Nemininingwane
Ishidi / Ipuleti / Umdweshu | I-ASTM B265 GR2
Din 17860 |
Ipayipi / Ishubhu engenamthungo | I-ASTM B337 (ihoxisiwe)
I-ASTM B338 GR2 I-SAE AMS 4942 I-SAE AMS 4943 I-ASTM B861 GR2 |
Ipayipi / Ipayipi elishiselwe | I-ASTM B862 GR2 Welded Tube |
Ibha eyisiyingi / Flat | Ibha ye-ASTM B348 Gr2
Din 17862 |
wire | Intambo ye-ASTM B863 GR2
I-ASTM B136 GR2 I-ASTM F67 Din 17863 |
Ukuxolelwa | ASTM B381 Gr2 forgings
Din 17864 |
Ukwenziwa kwamakhemikhali
Ti | C Max | Fe Max | H Max | N Max | O Max |
UKULINGANA | 0.08 | 0.30 | 0.015 | 0.05 | 0.02 |
Izakhiwo mechanical
Ubuningi | 4.51g/cc |
Ibanga lokuncibilika | Ubukhulu 1660 °C |
Amandla aqinile, imiz | 345 MPa |
Amandla esivuno, 0.2% offset, min, Mpa | 275 MPa |
I-Elongation at Break, % | 20 |
Ukuqina, Rockwell B | 160-200 HV |
Izicelo
I-Ti grade2 inikeza ibhalansi enhle kakhulu yamandla amaphakathi kanye ne-ductility enengqondo. Ilungele ukumelana nokugqwala embonini yamakhemikhali, engasogwini kanye neyezindiza lapho izinga elithile lamandla kanye nokwenza lula kwawo kufiseleka. Ibuye isetshenziswe ekushintsheni ukushisa, uhlelo lwe-hypochlorite, izinhlelo zamanzi omlilo, izinhlelo zamanzi ze-ballast, izibophelelo, izikhuphukeli, okokufakwayo, ama-flanges, ama-forging, amaphampu, ama-valve nokunye.