I-UNS S30815 Insimbi Engagqwali
I-UNS S30815/253MA/EN 1.4835 iyibanga elihlanganisa izakhiwo zesevisi ezinhle kakhulu emazingeni okushisa aphezulu kalula ukwenza. Imelana ne-oxidation emazingeni okushisa afinyelela ku-1150°C futhi inganikeza isevisi ephakeme kune-Grade 310 emkhathini we-carbon, nitrogen kanye nesibabule.
I-UNS S30815 iqukethe inani eliphansi le-nickel, elinikeza inzuzo ethile ekwehliseni umoya we-sulphide uma iqhathaniswa nama-alloys aphezulu e-nickel kanye neBanga 310.
Ukufakwa kwe-chromium ephezulu, i-silicon, i-nitrogen ne-cerium kunikeza ukuqina okuhle kwe-oxide okungu-253MA, amandla okushisa aphakeme (ukwenyuka) kanye nokumelana okuhle kakhulu nemvula yesigaba se-sigma. Isakhiwo se-austenitic sinikeza leli banga ukuqina okuhle kakhulu, ngisho naphansi kwamazinga okushisa e-cryogenic.
Ukwakhiwa kwamakhemikhali:
Ukwakheka kwekhemikhali (igama) %:
C | Si | Mn | P | S | Cr | Ni | N | Ce |
---|---|---|---|---|---|---|---|---|
0.08 | 1.6 | ≤0.8 | ≤0.040 | ≤0.030 | 21 | 11 | 0.17 | 0.05 |
Ku-cerium kufanele kwengezwe inani lezinye izinsimbi zomhlaba ezingavamile, kusukela ekuhlanganiseni
ithatha uhlobo lwensimbi ye-misch equkethe cishe u-50% Ce.
Izici zemishini:
ku-20°C:
Isivuno Amandla |
Amandla Amandla | Ukuphakanyiswa |
ubulukhuni |
|
Rp0.2 |
Rp1.0 | Rm | A | Ama-Vickers |
MPA |
MPA | MPA | % | |
≥310 | ≥350 | 650-850 | ≥40 |
≈190 |
ezingeni lokushisa eliphezulu:
Temperature |
Amandla obufakazi | Amandla Amandla | |
℃ |
Rp0.2 | Rp1.0 | Rm |
MPA |
MPA | MPA | |
100 |
≥225 | ≥265 | ≥550 |
200 |
≥189 | ≥215 |
≥475 |
300 | ≥170 | ≥200 |
≥440 |
400 | ≥160 | ≥190 |
≥425 |
500 | ≥150 | ≥180 |
≥400 |
600 | ≥140 | ≥165 |
≥340 |
ukwelashwa ukushisa
Isixazululo annealing 1020-1120ºC. Ukubamba isikhathi ekuxazululeni izinga lokushisa le-annealing cishe. 30 min., okulandelwa ukupholisa ngokushesha emoyeni noma emanzini.
Ukuphatha
Leli banga alikwazi ukwenziwa lukhuni ukwelashwa ngokushisa. Kodwa kungenziwa lukhuni ngokusebenza okubandayo.
yokukhiqiza
Ukwakheka okushisayo nokubandayo
Ukwakhiwa okushisayo kufanele kwenziwe ebangeni lokushisa lika-1150-900 ° C. Ukuvala isixazululo ngokuvamile akudingekile njengoba okokusebenza kuzovezwa kumazinga okushisa aphezulu uma kusebenza. Njengezinsimbi ezingenasici ezivamile ze-austenitic, izinto ezibonakalayo zingakhiwa kalula ezimweni ezibandayo. Ngenxa yokuqukethwe kwayo kwe-nitrogen ephezulu uma kuqhathaniswa, amandla emishini e-EN 1.4835 aphezulu futhi amandla okuguqula ayadingeka. Umshini Amandla obufakazi obuphakeme obuqhathaniswa be-EN 1.4835 kanye nokuthambekela kwayo ekubandeni kuqiniswe kufanele kucatshangelwe maqondana nokwenza imishini.
Amafomu Omkhiqizo:
Ipayipi neThubhu: ASTM A213, ASTM A312, EN 10216-5/EN 10217-7
Ipuleti, Ikhoyili yeshidi ne-Strip: ASTM A240/240M
Ukufakwa: ASTM A403 njenge-ASME B16.9
Ibha Eyindilinga, Ibha yesikwele: ASTM A276
Izicelo:
Amashubhu ezinhlelweni zokubuyisa ukushisa kukadoti embonini yensimbi, isb
Amashubhu ezithandweni zokushisa ukushisa, isb amashubhu emisebe, amashubhu okuvikela i-thermocouple, izingxenye zokushisisa, amarola wesithando somlilo
Amashubhu omjovo wamalahle ahlutshiwe ezithandweni eziqhumayo
Amashubhu wezitshalo ezishiswayo zombhede
Amashubhu esithandweni sezitshalo zokushiswa kodaka
Amashubhu e-carbon black process gas coolers/air heater
Amashubhu ezimboni zengilazi nezesimende
Amashubhu we-styrene reactor
EDC cracking amashubhu
Amashubhu e-convection ekuqhekekeni kwe-ethylene
Amashubhu okushisa komoya ku-sulfuric acid gas converters
Amashubhu e-muffle ezithandweni zokuhlanganisa izintambo eziqhubekayo